Plastic Testing Instruments
Aging Oven 61-PTI112
The maximum temperature : 300°C
Temperature fluctuation : Within ± 0.5°C
Temperature uniformity : Within ± 1°C
Rotate speed of the turntable : 11 r/min to 12r/min, turntable dimension diameter: 285 mm
Temperature fluctuation : Within ± 0.5°C
Temperature uniformity : Within ± 1°C
Rotate speed of the turntable : 11 r/min to 12r/min, turntable dimension diameter: 285 mm
Charpy/ Izod Impact Tester 61-PTI100
Impact Speed & Energy (charpy) : 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J
Impact energy (Izod) : 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J
Resolution of impact energy : 0.001 J
Pendulum up angle : 160°
Impact energy (Izod) : 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J
Resolution of impact energy : 0.001 J
Pendulum up angle : 160°
Heat sealer 61-PTI110
Seal temperature : Room temperature -250°C
Control accuracy : ± 0.2°C
Dwell time : 0.1 S to 999.9 S
Dwell pressure : 0.05 to 0.7 MPa
Control accuracy : ± 0.2°C
Dwell time : 0.1 S to 999.9 S
Dwell pressure : 0.05 to 0.7 MPa
Primary adhesive tester 61-PTI107
Inclined adjustable angle : 0 to 40°
Panel width : 120 mm
Test area width : 80 mm
Standard steel balls : 1/32 to 1 inch
Panel width : 120 mm
Test area width : 80 mm
Standard steel balls : 1/32 to 1 inch
Notch Cutter 61-PTI101
Cutting tool distance : 16 mm
Cutting tool parameter Model A : 45°± 30’ & r=0.25 ± 0.025
Cutting tool parameter Model B : 45°± 30’ & r=1.0 ± 0.025
Cutting tool thickness Model C : H=2 ± 0.1 & r≤0.1
Cutting tool parameter Model A : 45°± 30’ & r=0.25 ± 0.025
Cutting tool parameter Model B : 45°± 30’ & r=1.0 ± 0.025
Cutting tool thickness Model C : H=2 ± 0.1 & r≤0.1
Lasting adhesive tester 61-PTI108
Standard roller : 2000 ± 50 g
Testing stations : 3
Dimension (L*W*H) tester : 320×210×550 mm (3 stations)
Weight for stations : 10 kg (3 stations)
Testing stations : 3
Dimension (L*W*H) tester : 320×210×550 mm (3 stations)
Weight for stations : 10 kg (3 stations)
Lasting adhesive tester 61-PTI109
Standard roller : 2000 ± 50 g
Testing stations : 6
Dimension (L*W*H) tester : 650×210×550 mm (6 stations)
Weight for stations : 15 kg (6 stations)
Testing stations : 6
Dimension (L*W*H) tester : 650×210×550 mm (6 stations)
Weight for stations : 15 kg (6 stations)
Melt flow Indexer 61-PTI102
Measuring range : 0.01 to 600.00 g/ 10 min (MFR),
0.01 to 600.00 cm/ 10 min (MVR),
0.001 to 9.999 g/cm (melt density)
Measuring rate : 0.001 S
Temperature range : 50 to 400°C
Temperature precision : ± 0.5°C
Measuring rate : 0.001 S
Temperature range : 50 to 400°C
Temperature precision : ± 0.5°C
Melt flow Indexer 61-PTI103
Measuring range : 0.01to 600.00 g/ 10 min (MFR),
0.01 to 600.00 cm3/ 10 min (MVR),
0.001 to 9.999 g/ cm3 (melt density)
Measuring rate : 0.001 S
Temperature range : 50 to 400°C
Temperature precision : ± 0.5°C
Measuring rate : 0.001 S
Temperature range : 50 to 400°C
Temperature precision : ± 0.5°C
Vacuum Leak Tester 61-PTI104
Vacuum degree : 0 to 90 KPa
Accuracy : 1 % FS
Resolution : 0.1 Kpa
Vacuum chamber effective size : 270×200 mm
Accuracy : 1 % FS
Resolution : 0.1 Kpa
Vacuum chamber effective size : 270×200 mm
Oxygen Index Tester 61-PTI105
Resolution : 0.1 % O2
Measuring range : 0 to 100 % O2
Precision : ± 0.4 % O2
Response time : < 10 S
Measuring range : 0 to 100 % O2
Precision : ± 0.4 % O2
Response time : < 10 S
Falling Weight Impact Tester 61-PTI106
Temperature range : 10 to 35°C
Maximum falling height : 2000 mm
Resolution of displacement : 1 mm
Height error : < ± 2 mm
Maximum falling height : 2000 mm
Resolution of displacement : 1 mm
Height error : < ± 2 mm
Vicat softening temperature tester HDT 61-PTI111
Operating temperature : Ambient temperature to 300°C
Heating rate : 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min)
Maximum temp. error with heating speed : ± 5°C under 50°C/ h, ± 1°C under 120°C/ h
Range of deformation : 0 to 10 mm
Heating rate : 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min)
Maximum temp. error with heating speed : ± 5°C under 50°C/ h, ± 1°C under 120°C/ h
Range of deformation : 0 to 10 mm